SV-900 Industrial MS polymer silicone sealant
Short Description:
Description It is one component, primer less, can be painted, high quality joint sealant based on MS polymer technology, ideal for all sealing and boding on all materials. It is solvent free, environmental protection product. Where to use Sealing and bonding in housing area, bus, train, elevator, air conditioner, ventilation equipment. Used for installing fixed panel frame, windowsill threshold, and suitable for sealing on all materials surface, like painted metal, glass, wood, concret...
Our products are widely recognized and trusted by users and can meet continuously developing economic and social needs for SV-900 Industrial MS polymer silicone sealant, We sincerely welcome domestic and foreign merchants who calls, letters asking, or to plants to negotiate, we will offer you quality products and the most enthusiastic service,We look forward to your visit and your cooperation.
Description
It is one component, primer less, can be painted, high quality joint sealant based on MS polymer technology, ideal for all sealing and boding on all materials. It is solvent free, environmental protection product.
Where to use
Sealing and bonding in housing area, bus, train, elevator, air conditioner, ventilation equipment. Used for installing fixed panel frame, windowsill threshold, and suitable for sealing on all materials surface, like painted metal, glass, wood, concrete, marble, natural stone, granite, bricks, mirrors, aluminum, steel, lead, zinc, common plastics, polystyrene, polyurethane and so on. Sealing the joint of ceiling, timber, gaps of water pipe, gutter on roofs, moved rooms, container, marine. Apply for interior and exterior family decoration, like floor adhesive systems, particular for laying floor tiles, suitable for kitchen, bathroom.
Key Features
1. Paint able
2. Sealing most materials
3. Excellent adhesion
Technical data sheet
| Test standard | Test project | Unit | value |
| Before curing——25℃，50%R.H. | |||
| GB13477 | density | g/m³ | 1.40±0.05 |
| GB2793 | Non-volatile components | % | 99.5 |
| GB13477 | Flow, sagging or vertical flow | mm | 0 |
| GB13477 | surface drying time（25℃，50%R.H.） | min | 30 |
| Curing speed | mm/24h | 3 | |
| Sealant curing speed and operating time will have different with different temperatures and temperature, high temperature and high humidity can make sealant curing speed faster, rather low temperature and low humidity are slower.14days after curing——25℃，50%R.H. | |||
| GB13477 | Durometer Hardness | Shore A | 32-38 |
| GB13477 | The ultimate tensile strength | Mpa | 2.5 |
| GB13477 | elongation at break | % | 400 |
Color
White, black, grey
Package
300ml plastic cartridges
Shelf life
12 months
Note
If you want the TDS or MSDS or other details, please contact with our sales person.
Health and safety guidelines
Don’t will not curing sealant products in contact with the food, the cosmetics;
Not curing sealant not in contact with the skin for a long time;
If the sealant accidentally enter the eyes, must rinse immediately with plenty of water, and then send for a doctor check;
Place the product on children do not touch the place.
Method of use
Normally, universal and low modulus MSALL sealant without coat with the following materials: aluminium, stainless steel, coating, zinc, copper, brass, steel powder coating metal, painted metal, glass, PVC, polyester (GRP), spraying or painted wood glue is firm, but the material surface should be clean and dry, no ash, no oil.
Can’t glue unprocessed polyethylene, polypropylene and ptfe plastic surface. About cleaning agent and the use of the coat please consult zhijiang company technical personnel.
Shading performance
This product in the table can use the traditional way to dye after dry, including epoxy resin and acrylic coating dilute acid. Coating with high solvent composition, such as high gloss enamel or oil-based paint will result in soft rubber surface. It is recommended to use water-based environmental protection coating.
In order to get the best appearance and performance, coating must be close to the tensile ability of the product. With adhesive thickness less than 3 mm, can be in 24 hours after staining. For thickness is greater than 3 mm, can be in 48 hours after staining.