Special Price for SV-8890 Two-component Silicone Structural Glazing Sealant Supply to Washington

Sticking to the belief of "Creating products of high quality and making friends with people from all over the world", we always put the interest of customers in the first place for Special Price for SV-8890 Two-component Silicone Structural Glazing Sealant Supply to Washington, We will do our best to meet your requirements and are sincerely looking forward to developing mutual beneficial business relationship with you!

Description

SV8890 is neutral curing, designed for glass, stone, marble, granite, aluminum curtain wall and glass daylighting roof and metal structural engineering structural adhesive seal designed silicone sealant structure, excellent bonding performance of structure and the weathering resistance, after artificial accelerated weathering test, various physical and chemical properties have no obvious change in the sealant. When using, SV8890 with dedicated two-component glue machine construction, two kinds of components in accordance with the provisions, mixing ratio after curing form elastomer.

Key Features

1. None sag

2. Adjustable working time

3. Excellent adhesion to most building substrates

4. High bonding strength and modulus

5.12.5%movement capability

6. Silicone durability

Basic Application

1.Glass, stone, marble, granite, aluminum curtain wall and glass daylighting roof and metal structural engineering structural adhesive seal;

2.Insulating Glass of the second seal

3.Many other building and industrial applications

Technical data sheet

Certification

GB 16776

Color

Component A(Base) – White, Component B(Catalyst)- Black

Package

1. Component A(Base): (190L), Component B(Catalyst) (18.5L)

2. Component A(Base):24.5kg (18L), Component B(Catalyst): 1.9kg (1.8L)

Shelf life

12 months

Note

If you want the TDS or MSDS or other details, please contact with our sales person.

Installing Flexible or Insulated Duct is an easy DIY project. I’ll show you how to get the job done right. In this video, I use mastic and air duct sealant to reattach a flexible branch duct to my furnace’s main insulated duct.

Description:
　 HY630 is liquid rubber(condensation cure rtv, or tin cure silicone) mainly used for silicone plastic molds, with the advantages of good tensile strength, high tear strength, high temperature resistance, excellent chemical resistance, high duplication times, long-term stability, high durability, etc. This moulding rubber is one of the products with the highest use level in the production of craftwork gifts and its shrinkage is even lower than 2‰. RTV mould rubber and silicone rubber are general called two-component room temperature vulcanization silicone with excellent fluidity and good operational flexibility, easy moulding process, and so on. Add curing agent of 2%-3% at the room temperature, the rtv mould rubber is still operational within 30 minutes,and after 2-5 hours, the silicone elastomer(silicone mold) will be obtained with resistance to deformation, extremely high or low temperature, acid and alkali and expansion. The rtv mould rubber is mainly applicable to mold duplication of poly crafts, resin craftworks, lightings, candles. It is also suitable for fabrication of precision molds.

RTV Mould Rubber Applications:
Plastic molds, silicone soft plastic molds,making molds for plastic toys, plastic crafts, plastic gifts, PU products,stationary products, pavement, and so on. It has a quite broad applications due to its favorable viscosity and hardness.

RTV Mould Rubber Standard Datasheet:
Model
Appearance
Viscosity　 (cs)
Hardness (A°)
Tensile Strength (kgf/c㎡)
Tear Strength (kgf/㎝)
Elongation (%)
Mixing ratio(%)
Operating Time(H)
Curing Time(H)
630
White
30000~38000
30±2
≥3.8
≥2.8
≥380
2~3
0.5~1
2~5

Operation Instruction for rtv mould rubber:
　 The product is a kind of white flowing liquid . If the customer wants to make large products and large size molds, the mold should be made of rtv mould rubber with high hardness. On the contrary, if the mold with fine and precision patterns , it should be made of rtv mould rubber with low hardness. The amount of the curing agent depends on the actual requirements of the customer.

The proportions and reactions of the curing agent and the silicone are listed in the following:
　　1. Curing agent 1% added, the silicone can still be operated within 2.5 hours and can be demoulded after 6-8 hours.
　　2. Curing agent 2% added, the silicone can still be operated within 50 minutes to 1 hour and can be demoulded after 2-3 hours.
　　3. Curing agent 3% added, the silicone can still be operated within 28 – 30 minutes and can be demoulded after 1.5-2 hours.
　　4. Curing agent 4% added, the silicone can still be operated within 10 – 15 minutes and can be demoulded after 1 -1.5 hours.