SV-998 Polysulfide Sealant for Insulating Glass
Short Description:
Description It is a kind of two-part room temperature vulcanized polysulphide sealant with high performance especially formulated for insulating glass. This sealant has excellent elasticity, heat gas penetration and adherent stability to various glasses. Insulating glass is a kind of energy-efficient material with various functions of soundproof, heat-resistant,anti-frost,and anti-fumeetc.It is widely used as the wind shields in construction. trains automobiles and the door glasses in refrige...
We stick to our enterprise spirit of "Quality, Efficiency, Innovation and Integrity". We aim to create more value for our customers with our rich resources, advanced machinery, experienced workers and excellent services for SV-998 Polysulfide Sealant for Insulating Glass, We sincerely welcome domestic and foreign merchants who calls, letters asking, or to plants to negotiate, we will offer you quality products and the most enthusiastic service,We look forward to your visit and your cooperation.
Description
It is a kind of two-part room temperature vulcanized polysulphide sealant with high performance especially formulated for insulating glass. This sealant has excellent elasticity, heat gas penetration and adherent stability to various glasses.
Insulating glass is a kind of energy-efficient material with various functions of soundproof, heat-resistant,anti-frost,and anti-fumeetc.It is widely used as the wind shields in construction. trains automobiles and the door glasses in refrigerators and freezing cabins.
The property of SV-998 is certificated by JC/T486 -2001standard《elastic sealant for insulating glass》.
The product manufactured by SIWAY SV-998 is certificated by GB/T11944-2002 standard-《Insulating glass》.
Main Technical Properties (Only for Reference)
| Under the conditions of the 23+2 and the R.H.50+5% | ||||
| Item | Component A | Component B | ||
| Viscosity(Pa’s) | 100~300 | 30~150 | ||
| Appearance | Fine, smooth and homogeneous | fine, smooth and grease-like | ||
| Color | White | Black | ||
| Density(g/em3) | 1.75±0.1 | 1.52±0.1 | ||
| Mixed Component A and Component B at 10:1 by weight,under the conditions of 23±2℃ and the R.H. of 50±5% |
||||
| Item | Standard | Result | Test method | |
| Resistance to flow,mm | Vertical | ≤3 | 0.8 | GB/T113477 |
| level | No distortion | No distortion | ||
| Application Time, 30min, s | ≤10 | 4.8 | ||
|
A:B-10:1,Under the conditions of the 23+2℃and the R.H.of 50+5% after 7days of |
||||
| Item | Standard | Result | Test method | |
| Durometer hardness (Shore A) |
4h | 30 | GB/T1531 | |
| 24h | 40 | |||
| Tensile strength,MPa | MPa | 0.8 | GB/T113477 | |
|
Permeation rate of evaporation(g/m2.d) |
≤15 | 8 | GB/T11037 | |
| GB/T113477 | 25HM | JC/T1 486 | ||
| GB/T1Chinese national standard | ||||
Packing
SV-998 Polysulphide sealant is available as:
Packing 1:Component A:300kgsteel drum Component B:30kgsteel drum
Packing 2:Component A:30ka steel drumComponent B:3ka/plastic pail
Shelf Life Storage
When stored at or below 27℃ in the original unopened containers this product has a shelf life of12 months from the date of production.
Precautions
Avoid direct contact with food and cosmetic.
Avoid prolonged skin contact with uncured sealant.
The uncured sealant should not contact with eyes and mouthIf sealant gets into eyes, flush with water. See dhysician ifnecessary.
Ensure good ventilation if used indoor.
Keep out of reach of Children
SV998 Polysulphide sealant is specially designed for insulating glass.
Application
1.Two parts of SIWAY S-998 packaged respectively of composition A(basic gel) and a composition B(curing agent), are mixed together according to the ratio of A:B=10:1 before application. The curing rate may be modulated by changing the weight ratio of composition A to composition B over the range of 12:1 to 8:1 according to different environment conditions
2. The mixture of sealant can be classified into two methods one by hand-made and the other by special extrusion machine. It is noticed that SIWAY SV-998 sealant should be scratched and mixed by the spatula along the same direction repeatedly to prevent gas bubble trapped in sealant in the method of hand-made.The homogeneity of mixture can be measured bybutterfly-type method as listed in the following figure:
Good Mixture Bad Mixture
3. The surfaces of insulating glasses must be dry and clean.
4.SIWAY SV-998 should fill the joints completely which need to be caulked during the course of making insulating glass.
5.Gun mouth should be assured to move along the same direction at uniform velocity to make the ioints full of sealant and prevent the gas bubble production due to moving too fast or back and forth in the method ofusing special extrusion machine.
6. The sealant overflowing the joints should be pressed back at once by spatula to make the sealant contacting with the sides of the joints completely and smooth the surface of the joints along the same direction.