High Performance SV-8890 Two-component Silicone Structural Glazing Sealant Wholesale to Slovak Republic
Short Description:
Description SV8890 is neutral curing, designed for glass, stone, marble, granite, aluminum curtain wall and glass daylighting roof and metal structural engineering structural adhesive seal designed silicone sealant structure, excellent bonding performance of structure and the weathering resistance, after artificial accelerated weathering test, various physical and chemical properties have no obvious change in the sealant. When using, SV8890 with dedicated two-component glue machine constructi...
Our products are widely recognized and trusted by users and can meet continuously changing economic and social needs for High Performance SV-8890 Two-component Silicone Structural Glazing Sealant Wholesale to Slovak Republic, Competitive price with high quality and satisfying service make us earned more customers.we wish to work with you and seek common development.
Description
SV8890 is neutral curing, designed for glass, stone, marble, granite, aluminum curtain wall and glass daylighting roof and metal structural engineering structural adhesive seal designed silicone sealant structure, excellent bonding performance of structure and the weathering resistance, after artificial accelerated weathering test, various physical and chemical properties have no obvious change in the sealant. When using, SV8890 with dedicated two-component glue machine construction, two kinds of components in accordance with the provisions, mixing ratio after curing form elastomer.
Key Features
1. None sag
2. Adjustable working time
3. Excellent adhesion to most building substrates
4. High bonding strength and modulus
5.12.5%movement capability
6. Silicone durability
Basic Application
1.Glass, stone, marble, granite, aluminum curtain wall and glass daylighting roof and metal structural engineering structural adhesive seal;
2.Insulating Glass of the second seal
3.Many other building and industrial applications
Technical data sheet
Test project | Unit | value |
Flow, sagging or vertical flow | mm | 0 |
Operating time | min | 20 |
surface drying time(25℃,50%R.H.) | min | 40-60 |
Durometer Hardness | Shore A | 20-60 |
At 23 ℃ maximum tensile strength elongation | % | ≥100 |
Tensile strength(23℃) | Mpa | 0.9 |
Tensile strength(90℃) | Mpa | 0.68 |
Tensile strength(-30℃) | Mpa | 0.68 |
Tensile strength(flooding) | Mpa | 0.68 |
Tensile strength(flooding – ultraviolet) | Mpa | 0.68 |
Bond damage area | % | 5 |
Thermal aging(thermal weight loss) | % | ≤5 |
Thermal aging(crack) | No | |
Thermal aging(efflorescence) | No |
Certification
GB 16776
Color
Component A(Base) – White, Component B(Catalyst)- Black
Package
1. Component A(Base): (190L), Component B(Catalyst) (18.5L)
2. Component A(Base):24.5kg (18L), Component B(Catalyst): 1.9kg (1.8L)
Shelf life
12 months
Note
If you want the TDS or MSDS or other details, please contact with our sales person.
How to repair vinyl tarps
A little life hack I recently figured out while refinishing furniture using Minwax furniture refinisher solvent on some old furniture. The stuff is made to dissolve fully cured air dry polymers and does a pretty good job at it. It evaporates and soaks into stuff quickly so you have to work fast with it using steel wool instead of cloth, more on that in the wood refinishing videos tomorrow, but I discovered this is good stuff for getting that expanding foam out of cloth. That stuff is extremely sticky and hard to remove. The solvent works (but not quite as well) on liquid nails too. It is best to scrape the stuff down with a knife prior to using the solvent on it or else it will take too much solvent to dissolve the foam or liquid nails. It does not work as well on latex paint, so this is part of matching the chemical to the job.