8 Years Manufacturer SV-8890 Two-component Silicone Structural Glazing Sealant for Iran Factories
Short Description:
Description SV8890 is neutral curing, designed for glass, stone, marble, granite, aluminum curtain wall and glass daylighting roof and metal structural engineering structural adhesive seal designed silicone sealant structure, excellent bonding performance of structure and the weathering resistance, after artificial accelerated weathering test, various physical and chemical properties have no obvious change in the sealant. When using, SV8890 with dedicated two-component glue machine constructi...
Our target is to consolidate and improve the quality and service of existing products, meanwhile constantly develop new products to meet different customers' demands for 8 Years Manufacturer SV-8890 Two-component Silicone Structural Glazing Sealant for Iran Factories, We cordially welcome customers from at home and abroad to join us and cooperate with us to enjoy a better future.
Description
SV8890 is neutral curing, designed for glass, stone, marble, granite, aluminum curtain wall and glass daylighting roof and metal structural engineering structural adhesive seal designed silicone sealant structure, excellent bonding performance of structure and the weathering resistance, after artificial accelerated weathering test, various physical and chemical properties have no obvious change in the sealant. When using, SV8890 with dedicated two-component glue machine construction, two kinds of components in accordance with the provisions, mixing ratio after curing form elastomer.
Key Features
1. None sag
2. Adjustable working time
3. Excellent adhesion to most building substrates
4. High bonding strength and modulus
5.12.5%movement capability
6. Silicone durability
Basic Application
1.Glass, stone, marble, granite, aluminum curtain wall and glass daylighting roof and metal structural engineering structural adhesive seal;
2.Insulating Glass of the second seal
3.Many other building and industrial applications
Technical data sheet
| Test project | Unit | value |
| Flow, sagging or vertical flow | mm | 0 |
| Operating time | min | 20 |
| surface drying time（25℃，50%R.H.） | min | 40-60 |
| Durometer Hardness | Shore A | 20-60 |
| At 23 ℃ maximum tensile strength elongation | % | ≥100 |
| Tensile strength（23℃） | Mpa | 0.9 |
| Tensile strength（90℃） | Mpa | 0.68 |
| Tensile strength（-30℃） | Mpa | 0.68 |
| Tensile strength（flooding） | Mpa | 0.68 |
| Tensile strength（flooding – ultraviolet） | Mpa | 0.68 |
| Bond damage area | % | 5 |
| Thermal aging（thermal weight loss） | % | ≤5 |
| Thermal aging（crack） | No | |
| Thermal aging（efflorescence） | No |
Certification
GB 16776
Color
Component A(Base) – White, Component B(Catalyst)- Black
Package
1. Component A(Base): (190L), Component B(Catalyst) (18.5L)
2. Component A(Base):24.5kg (18L), Component B(Catalyst): 1.9kg (1.8L)
Shelf life
12 months
Note
If you want the TDS or MSDS or other details, please contact with our sales person.
Complete instructions for intake manifold swap on 4.6l Ford V8 engine. It is easy! I got new Dorman 615-175 to replace stock OEM part. Each step was relatively easy but there were a lot of steps. Took me 6 hours total for removal and repair. The Dorman part came with new thermostat and O-ring. Also had new alternator bracket as old one could not be used. This part is improved over original OE as has O-rings for all ports so a gasket is not needed. No more leaking coolant. Fits 2001, 2002, 2003, 2004, 2005, 2006, 2007, 2008, 2009 and 2010 Crown Victoria and other Ford, Lincoln, Mercury V8 motors such as Mustang, Explorer, Expedition, Grand Marquis, Town Car. The 5.4l truck and Expedition should be similar.
Rub-R-Wall foundation coating sprayed on by Advanced Foundation Coatings. .
LET’S CONNECT!
God’s Country’s Accounts:
- https://gplus.to/GodsCountry
- https://www.facebook.com/godscountrychannel
- https://twitter.com/In_Gods_Country