22 Years Factory SV-999 Structural Glazing Silicone Sealant for Algeria Manufacturers
Short Description:
Description SV – 999 silicone structural sealant is a one-component, neutral curing, designed for glass curtain wall, aluminum curtain wall, glass daylighting roof and metal structural engineering structural assembly silicone sealant. Show the effective physical properties and bonding performance Key Features 1. 100% silicone 2. No sag 3. Strong bonding strength 4. Water & weatherproof 5. Primerless adhesion to most building materials 6. 25% movement capability Basic Application...
We have many excellent staff members good at marketing, QC, and dealing with kinds of troublesome problem in the production process for 22 Years Factory SV-999 Structural Glazing Silicone Sealant for Algeria Manufacturers, Welcome to visit us at any time for business relationship established.
Description
SV – 999 silicone structural sealant is a one-component, neutral curing, designed for glass curtain wall, aluminum curtain wall, glass daylighting roof and metal structural engineering structural assembly silicone sealant. Show the effective physical properties and bonding performance
Key Features
1. 100% silicone
2. No sag
3. Strong bonding strength
4. Water & weatherproof
5. Primerless adhesion to most building materials
6. 25% movement capability
Basic Application
1.Glass curtain wall, aluminum curtain wall structure adhesive seal
2.Glass daylighting roof, metal structure engineering
3.Insulating glass bonding
Technical data sheet
| Test standard | Test project | Unit | value |
| Before curing——25℃，50%R.H. | |||
| specific gravity | g/ml | 1.40 | |
| GB13477 | Flow, sagging or vertical flow | mm | 0 |
| GB13477 | Operating time | min | 15 |
| GB13477 | surface drying time（25℃，50%R.H.） | min | 40-60 |
| Sealant curing speed and operating time will have different with different temperatures and temperature, high temperature and high humidity can make sealant curing speed faster, rather low temperature and low humidity are slower.21 days after curing——25℃，50%R.H. | |||
| GB13477 | Durometer Hardness | Shore A | 40 |
| The ultimate tensile strength | Mpa | 1.3 | |
| GB13477 | Tensile strength（23℃） | Mpa | 0.8 |
| GB13477 | Tensile strength（90℃） | Mpa | 0.5 |
| GB13477 | Tensile strength（-30℃） | Mpa | 0.9 |
| GB13477 | Tensile strength（flooding） | Mpa | 0.6 |
| GB13477 | Tensile strength（flooding – ultraviolet） | Mpa | 0.6 |
Certification
GB 16776；ASTM C1184
Color
Black
Package
300ml in cartridge * 24 per box, 500ml in sausage *20 per box
Shelf life
12 months
Note
If you want the TDS or MSDS or other details, please contact with our sales person.
I started with one idea in the beginning of this video (the battery charger was going to be Hal, talking to me and watching me do a project, while I became increasingly unsettled), but decided to go in another direction part of the way through when the foam idea came to me.
While dissolving the foam, I thought it would be interesting to use it as end grain sealer on the log pieces, so added that in.
Normally, I have the video planned out before I get started, but went with the flow this time.
The “lacquer” itself is not bad, for what it was made from. I think it make a fairly good clear finish, if it was filtered. It dried surprising hard and glossy, and since it’s plastic, would be fairly water resistant.
I used roughly half of the 1 gallon can to dissolve the foam, and did it outdoors for ventilation. Lacquer thinner is a strong solvent and very flammable (especially in combination with the foam), so keeping it away from open flames or sparks will help to keep it from becoming a much more interesting day.