2017 China New Design SV-8890 Two-component Silicone Structural Glazing Sealant for Egypt Factory
Short Description:
Description SV8890 is neutral curing, designed for glass, stone, marble, granite, aluminum curtain wall and glass daylighting roof and metal structural engineering structural adhesive seal designed silicone sealant structure, excellent bonding performance of structure and the weathering resistance, after artificial accelerated weathering test, various physical and chemical properties have no obvious change in the sealant. When using, SV8890 with dedicated two-component glue machine constructi...
With a complete scientific quality management system, good quality and good faith, we win good reputation and occupied this field for 2017 China New Design SV-8890 Two-component Silicone Structural Glazing Sealant for Egypt Factory, We are looking forward to establishing long-term business relationships with you. Your comments and suggestions are highly appreciated.
Description
SV8890 is neutral curing, designed for glass, stone, marble, granite, aluminum curtain wall and glass daylighting roof and metal structural engineering structural adhesive seal designed silicone sealant structure, excellent bonding performance of structure and the weathering resistance, after artificial accelerated weathering test, various physical and chemical properties have no obvious change in the sealant. When using, SV8890 with dedicated two-component glue machine construction, two kinds of components in accordance with the provisions, mixing ratio after curing form elastomer.
Key Features
1. None sag
2. Adjustable working time
3. Excellent adhesion to most building substrates
4. High bonding strength and modulus
5.12.5%movement capability
6. Silicone durability
Basic Application
1.Glass, stone, marble, granite, aluminum curtain wall and glass daylighting roof and metal structural engineering structural adhesive seal;
2.Insulating Glass of the second seal
3.Many other building and industrial applications
Technical data sheet
| Test project | Unit | value |
| Flow, sagging or vertical flow | mm | 0 |
| Operating time | min | 20 |
| surface drying time（25℃，50%R.H.） | min | 40-60 |
| Durometer Hardness | Shore A | 20-60 |
| At 23 ℃ maximum tensile strength elongation | % | ≥100 |
| Tensile strength（23℃） | Mpa | 0.9 |
| Tensile strength（90℃） | Mpa | 0.68 |
| Tensile strength（-30℃） | Mpa | 0.68 |
| Tensile strength（flooding） | Mpa | 0.68 |
| Tensile strength（flooding – ultraviolet） | Mpa | 0.68 |
| Bond damage area | % | 5 |
| Thermal aging（thermal weight loss） | % | ≤5 |
| Thermal aging（crack） | No | |
| Thermal aging（efflorescence） | No |
Certification
GB 16776
Color
Component A(Base) – White, Component B(Catalyst)- Black
Package
1. Component A(Base): (190L), Component B(Catalyst) (18.5L)
2. Component A(Base):24.5kg (18L), Component B(Catalyst): 1.9kg (1.8L)
Shelf life
12 months
Note
If you want the TDS or MSDS or other details, please contact with our sales person.
Product review of Blue stuff silicone rubber and RAW material suppliers Silicone rubber.Over all the Blue Stuff is easy to use and has better results but is a tad more cash.Also the mix was alot more forgiving with the blue stuff.If you did not get the mix right the RAW MS silicone would not harden very well.After a few trys i figured it out tho.
How to use a gram scale to accurately weigh rubbers, plastics and other materials.
Gram scales are available in a wide range of sizes, weight capacities, and prices. Place measuring container on scale. Press the “tare” button to reset scale to zero grams.
Mold Max 20 mix ratio is 100A:10B by weight.
Material is carefully dispensed. Remove any excess material if necessary until desired weight is achieved. 330 grams of Part A were dispensed. 33 grams of Part B will be dispensed. Press the “tare” button to reset the scale to zero grams. Material is carefully dispensed.
Combine Parts A & B. You are now ready to mix.
Make It Now! with Smooth-On
https://www.smooth-on.com/
https://www.facebook.com/SmoothOn
https://twitter.com/SmoothOn
https://www.google.com/+smoothon