15 Years Factory SV-999 Structural Glazing Silicone Sealant to Angola Manufacturers
Short Description:
Description SV – 999 silicone structural sealant is a one-component, neutral curing, designed for glass curtain wall, aluminum curtain wall, glass daylighting roof and metal structural engineering structural assembly silicone sealant. Show the effective physical properties and bonding performance Key Features 1. 100% silicone 2. No sag 3. Strong bonding strength 4. Water & weatherproof 5. Primerless adhesion to most building materials 6. 25% movement capability Basic Application...
Our development depends on the advanced equipment, excellent talents and continuously strengthened technology forces. 15 Years Factory SV-999 Structural Glazing Silicone Sealant to Angola Manufacturers, With a wide range, good quality, reasonable prices and good service, we will be your best business partner. We welcome new and old customers from all walks of life to contact us for future business relationships and achieving mutual success!
Description
SV – 999 silicone structural sealant is a one-component, neutral curing, designed for glass curtain wall, aluminum curtain wall, glass daylighting roof and metal structural engineering structural assembly silicone sealant. Show the effective physical properties and bonding performance
Key Features
1. 100% silicone
2. No sag
3. Strong bonding strength
4. Water & weatherproof
5. Primerless adhesion to most building materials
6. 25% movement capability
Basic Application
1.Glass curtain wall, aluminum curtain wall structure adhesive seal
2.Glass daylighting roof, metal structure engineering
3.Insulating glass bonding
Technical data sheet
| Test standard | Test project | Unit | value |
| Before curing——25℃，50%R.H. | |||
| specific gravity | g/ml | 1.40 | |
| GB13477 | Flow, sagging or vertical flow | mm | 0 |
| GB13477 | Operating time | min | 15 |
| GB13477 | surface drying time（25℃，50%R.H.） | min | 40-60 |
| Sealant curing speed and operating time will have different with different temperatures and temperature, high temperature and high humidity can make sealant curing speed faster, rather low temperature and low humidity are slower.21 days after curing——25℃，50%R.H. | |||
| GB13477 | Durometer Hardness | Shore A | 40 |
| The ultimate tensile strength | Mpa | 1.3 | |
| GB13477 | Tensile strength（23℃） | Mpa | 0.8 |
| GB13477 | Tensile strength（90℃） | Mpa | 0.5 |
| GB13477 | Tensile strength（-30℃） | Mpa | 0.9 |
| GB13477 | Tensile strength（flooding） | Mpa | 0.6 |
| GB13477 | Tensile strength（flooding – ultraviolet） | Mpa | 0.6 |
Certification
GB 16776；ASTM C1184
Color
Black
Package
300ml in cartridge * 24 per box, 500ml in sausage *20 per box
Shelf life
12 months
Note
If you want the TDS or MSDS or other details, please contact with our sales person.
https://go.askthebuilder.com/NewsletterSignupNow founder, Tim Carter describes the importance of a treated lumber sill plate in a wood-framed house.
Get FREE tips like this by subscribing to Tim’s FREE newsletter now. Go to: https://go.askthebuilder.com/NewsletterSignupNow
Discover more about sills at askthebuilder.com:
https://www.askthebuilder.com/temporary-partition-wall/
https://www.askthebuilder.com/brick-leaks/
https://www.askthebuilder.com/floor-joist-best-practices/
Before applying waterproofing co-polymer base coating surface of newly built roof cheeped by
knocking impact of chiseler manually without leaving any portion of roof left from this process
of cheeping.This process applied because while doing plaster & preparation of mortar some portion of mortar impregnated on top surface of roof slabs for good bonding of coating surface of roof should be free from loose particle or surface.