Description SV8890 is neutral curing, designed for glass, stone, marble, granite, aluminum curtain wall and glass daylighting roof and metal structural engineering structural adhesive seal designed silicone sealant structure, excellent bonding performance of structure and the weathering resistance, after artificial accelerated weathering test, various physical and chemical properties have no obvious change in the sealant. When using, SV8890 with dedicated two-component glue machine constructi...
It is a good way to improve our products and service. Our mission is to develop creative products to customers with a good experience for 100% Original Factory SV-8890 Two-component Silicone Structural Glazing Sealant Export to Sydney, We welcome customers, business associations and friends from all parts of the world to contact us and seek cooperation for mutual benefits.
Description
SV8890 is neutral curing, designed for glass, stone, marble, granite, aluminum curtain wall and glass daylighting roof and metal structural engineering structural adhesive seal designed silicone sealant structure, excellent bonding performance of structure and the weathering resistance, after artificial accelerated weathering test, various physical and chemical properties have no obvious change in the sealant. When using, SV8890 with dedicated two-component glue machine construction, two kinds of components in accordance with the provisions, mixing ratio after curing form elastomer.
Key Features
1. None sag
2. Adjustable working time
3. Excellent adhesion to most building substrates
4. High bonding strength and modulus
5.12.5%movement capability
6. Silicone durability
Basic Application
1.Glass, stone, marble, granite, aluminum curtain wall and glass daylighting roof and metal structural engineering structural adhesive seal;
2.Insulating Glass of the second seal
3.Many other building and industrial applications
Technical data sheet
| Test project | Unit | value |
| Flow, sagging or vertical flow | mm | 0 |
| Operating time | min | 20 |
| surface drying time（25℃，50%R.H.） | min | 40-60 |
| Durometer Hardness | Shore A | 20-60 |
| At 23 ℃ maximum tensile strength elongation | % | ≥100 |
| Tensile strength（23℃） | Mpa | 0.9 |
| Tensile strength（90℃） | Mpa | 0.68 |
| Tensile strength（-30℃） | Mpa | 0.68 |
| Tensile strength（flooding） | Mpa | 0.68 |
| Tensile strength（flooding – ultraviolet） | Mpa | 0.68 |
| Bond damage area | % | 5 |
| Thermal aging（thermal weight loss） | % | ≤5 |
| Thermal aging（crack） | No | |
| Thermal aging（efflorescence） | No |
Certification
GB 16776
Color
Component A(Base) – White, Component B(Catalyst)- Black
Package
1. Component A(Base): (190L), Component B(Catalyst) (18.5L)
2. Component A(Base):24.5kg (18L), Component B(Catalyst): 1.9kg (1.8L)
Shelf life
12 months
Note
If you want the TDS or MSDS or other details, please contact with our sales person.
After paying $199 for the last repair, I decided to try my hand at the repair when a golf ball came through the window this afternoon. This is definitely a lot easier than it initially appeared.
Updated 7/18/2015:
I had another ball come through the window this week and I have posted a follow-up repair:
-B
MotorWeek’s Pat Goss (RockAuto.com is a MotorWeek Sponsor) shows what to avoid when removing old gaskets from aluminum cylinder heads and other aluminum car parts.